Beton proportionering

Question 1

What are the typical components of a concrete mix?

Answer 1

A concrete mix typically consists of cement, water, sand, and stone.

Question 2

What is the most important factor affecting concrete strength?

Answer 2

The most important factor is the water-cement ratio (w/c ratio). Typical values range from 0.35 to 0.60.

Question 3

What is the significance of the strength of aggregates (sand and stone) in concrete?

Answer 3

The aggregates must have greater strength than the finished concrete. Using more porous stones (lighter than 2400kg/m3) will reduce strength.

Question 4

How does the choice of aggregates affect concrete durability?

Answer 4

The choice of aggregates significantly influences durability. For example, using frost-susceptible stones or porous flint can lead to alkali-silica reactions.

Question 5

Hvorfor blandes microsilica og flyveaske i betonen?

Answer 5

Det er billigere end cement. Det forbedrer bearbejdeligheden og giver en tættere beton, som øger holdbarheden.

Question 6

Hvad gør microsilica og flyveaske ved betonens egenskaber?

Answer 6

Det giver en tættere beton, som øger holdbarheden. Det reagerer langsommere og giver derved en mindre varmeudvikling.

Question 7

Hvorfor er der en maksimal grænse for indholdet af microsilica og flyveaske i nogle af miljoklasserne?

Answer 7

Microsilica og flyveaske reagerer kun med vandet, hvis der er tilstrækkelig mængde cement, derfor er der indført grænser.

Question 8

Hvad er et modenhedsdogn?

Answer 8

Et modenhedsdogn: 24 timer ved med en temperatur på 20 og RF på 100%

Question 9

Hvad er hastighedsfaktoren for en størrelse?

Answer 9

Hastighedsfaktoren er et mål for, hvor hurtigt en størrelse ændrer sig over tid.

Question 10

Hvad bruges hastighedsfaktoren til?

Answer 10

Hastighedsfaktoren bruges til at vurdere væksten af afgrøder under forskellige forhold.

Question 11

Hvad svarer 10 dogn ved 15 grader til?

Answer 11

10 dogn ved 15 grader svarer til en specifik vækstperiode for afgrøder.

Question 12

Hvad skal man være opmærksom på når man stober beton?

Answer 12

Temperatur, risiko for frost.

Question 13

Hvad skal man sikre sig for at undgå fordampning fra betonoverfladen?

Answer 13

Afdakningsbeskyttelse.

Question 14

Hvad er vigtigt for komprimering af beton?

Answer 14

Tilstrækkelig komprimering.

Question 15

Hvor lang tid skal betonen blandes?

Answer 15

Tilstrækkelig blandetid.

Question 16

Hvordan skal stobeformen udføres?

Answer 16

Stobeformen skal udføres så betonen løber let.

Question 17

Hvordan beregnes betons styrke?

Answer 17

Styrken kan beregnes efter Bolomeys eller Neppers Formel. Bolomeys er mest simpel og kan bruges til at finde styrken efter 28 modenhedsdegn.

Question 18

Hvad betyder det, når en beton betegnes som beton35?

Answer 18

En Beton35 har en karakteristisk (cylinder) trykstyrke på 35MPa efter 28 modenhedsdegn.

Question 19

Hvornår kan styrken også findes for Aalborg Portland cementer?

Answer 19

Styrken kan også findes efter 1 og 7 degn.

Question 20

Hvad er forskellen på betons trækstyrke og trykstyrke?

Answer 20

Betons trykstyrke er 10-20 gange større end trækstyrke.

Question 21

Hvordan armeres beton, når den udsættes for trækpåvirkning?

Answer 21

Beton armeres med armeringsjern eller armeringsfibre, der kan optage trækkræfter.

Question 22

Hvad er sætmäl?

Answer 22

Sætmäl bruges for almindelig beton.

Question 23

Hvad er flydemäl?

Answer 23

Flydemäl bruges for flydebeton SCC.

Question 24

Hvad fortæller sætmäl og flydemäl os om betonen?

Answer 24

Det fortæller os om bearbejdeligheden. Des større sætmäl, des mere bearbejdelig.

Question 25

Hvad er armeret beton?

Answer 25

Armeret beton er beton der er forstærket med armering.

Question 26

Hvilke typer armering findes der?

Answer 26

Armering er typisk stålstænger, eller mindre traditionelt stål- eller plastfibre.

Question 27

Hvad bruges armeringen til?

Answer 27

Armeringen bruges til at optage trak- eller forskydningskrafter.

Question 28

How does air content affect concrete strength?

Answer 28

For every 1% increase in air content, there is a decrease in strength of 4-5%.

Question 29

What is the relationship between air content and workability of concrete?

Answer 29

More air in the concrete makes it more workable, allowing for a reduction in water content, which increases strength.

Question 30

How does air content affect frost resistance in concrete?

Answer 30

The more air content in the concrete, the more frost-resistant it is.

Question 31

What is the natural air content in concrete?

Answer 31

The natural air content in concrete is typically 1-2%.

Question 32

How can air be added to concrete?

Answer 32

Air can be added by using an air-entraining agent, typically aiming for an air content of 4-6%.

Question 33

Hvorfor er det vigtigt at kende tilslagets vandindhold og absorption?

Answer 33

For at få det ønskede vand/cement-forhold skal tilslagets vandindhold og absorption kendes.

Question 34

Hvad sker der, hvis der er for meget vand i tilslaget?

Answer 34

Hvis der er for meget vand i tilslaget, vil dette vand afgives til betonen, hvilket øger den samlede vandmængde og dermed v/c-forholdet, som medfører mindre styrke.

Question 35

Hvad sker der, hvis tilslaget har mindre vandindhold end det kan absorbere?

Answer 35

Tilslaget vil absorbere (suge) vand til sig, hvilket vil sænke v/c-forholdet og medføre større styrke, men også mindre bearbejdelighed.

Question 36

Hvordan kan betonrecepten reguleres?

Answer 36

Når absorptionen og vandindholdet kendes, kan betonrecepten reguleres, så det ønskede v/c-forhold bibeholdes.

Question 37

Hvordan findes tilslagets absorptionsevne?

Answer 37

Tilslagets absorptionsevne findes ved at bringe tilslaget i vandmættet overfladetor tilstand (VOT). Det vejes, terres og vejes igen, og absorptionsevnen kan beregnes.

Question 38

Hvad bruges tilslagets absorptionsevne til?

Answer 38

Absorptionsevnen bruges til at kunne regulere betonrecepten, således at det ønskede v/c-forhold bibeholdes.

Question 39

Hvad er filler i beton?

Answer 39

Filler er korn mindre end 1/4mm.

Question 40

Hvordan påvirker filler betonens egenskaber?

Answer 40

Filler øger tæthed og dermed også holdbarheden af beton.

Question 41

Hvilken negativ effekt har filler på beton?

Answer 41

Filler giver et forhøjet vandbehov, hvilket ikke er ønskeligt.

Question 42

Hvorfor er der krav til fillerindholdet i aggressive miljøklasser?

Answer 42

Der er krav til fillerindholdet for at sikre betonens holdbarhed i aggressive og ekstra aggressive miljøer.

Question 43

Hvad er miljoklasser?

Answer 43

Miljoklasser definerer hvilket miljø betonen vil være i.

Question 44

Hvad bestemmer hvilken miljoklasse beton henhorer til?

Answer 44

Det bestemmes af vejrlig (vand og frost), kemiske påvirkninger mv.

Question 45

Hvad har indflydelse på betons holdbarhed?

Answer 45

Det miljø som beton er i har meget at sige. Hvis en betonbjælke er placeret udvendigt i saltvand, er dens levetid kortere end hvis den var placeret i tørt klima.

Question 46

Hvordan påvirker betonens sammensætning holdbarheden?

Answer 46

Desto tættere beton, des bedre holdbarhed. Tæthed af beton øges med mere fillerindhold, mindre vand, mere cement, og mere flyveaske.

Question 47

Hvordan kan risikoen for korrosion i armeringen nedsættes?

Answer 47

Risiko for korrosion i armeringen skal nedsættes for at øge holdbarheden. Derfor kan dæklaget øges og chloridindholdet minimeres.

Question 48

Hvad skal undgås for at forhindre alkalikiselreaktioner?

Answer 48

For at undgå alkalikiselreaktioner skal man undgå at bruge pores flint som tilslagsmateriale.

Question 49

Hvad skal man være opmærksom på under udstøbningen af beton?

Answer 49

Under udstøbningen skal man være opmærksom på at få betonen komprimeret tilstrækkeligt, undgå frostskader og undgå udtørring ved at afdække betonen.

Question 50

Hvad er forskellen på et sejt og et spredt materiale?

Answer 50

Et sejt materiale kan deformeres meget uden at bryde, mens et spredt materiale bryder efter kun en lille deformation.

Question 51

Hvad foretrækker vi, når materialet anvendes til bærende konstruktioner?

Answer 51

Vi foretrækker seje materialer, da de giver forvarsel om overbelastning før brud.

Question 52

Hvad sker der med et sejt materiale ved overbelastning?

Answer 52

Det deformeres meget, hvilket giver mulighed for at evakuere bygningen før den bryder.

Question 53

Hvad er risikoen ved et spredt materiale?

Answer 53

Et spredt materiale vil bryde næsten uden forvarsel, hvilket medfører større risiko for personskader.